塑胶原料 > 产品分类 > 铁氟龙PEKK聚醚酮酮

OXPEKK® Permetta™ Film SP

OXPEKK® Permetta™ Film SP

2020-08-07

OXPEKK® Permetta™ Film SP      
Polyetherketoneketone      
Product Description
Superior Electrical Properties
 
Highly Formable Matrix
 
High Tg
 
Flame Retardant UL94 V-0 Rated
 
OSU 65/65 Compliant
 
Excellent Adhesive Performance
 
General  
       
Flame Retardant Good Electrical Properties
   
Agency Ratings  OSU 65/65
Appearance  Amber
Forms  Preformed Parts

Physical Nominal Value Unit Test Method
Specific Gravity 1.28 g/cm³ ASTM D792
Melt Mass-Flow Rate (MFR) (380°C/8.4 kg) 35 to 45 g/10 min ASTM D1238
Molding Shrinkage - Flow  < 0.50 % ASTM D955
Water Absorption (24 hr) < 0.20 % ASTM D570
Hardness Nominal Value Unit Test Method
Rockwell Hardness (M-Scale) 86   ASTM D785
Mechanical Nominal Value Unit Test Method
Tensile Modulus 3450 MPa ASTM D638
Tensile Strength     ASTM D638
Break 2 11.9 MPa  
Break 3 17.9 MPa  
Break 89.6 MPa  
Break 4 6.96 MPa  
Break 5 9.51 MPa  
Break 6 10.5 MPa  
Tensile Elongation (Break) 80 % ASTM D638
Flexural Modulus 3380 MPa ASTM D790
Flexural Strength (Yield) 138 MPa ASTM D790
Compressive Strength 103 MPa ASTM D695
Coefficient of Friction (vs. Itself - Static) 0.29   ASTM D1894
Impact Nominal Value Unit Test Method
Notched Izod Impact 48 J/m ASTM D256
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed) 141 °C ASTM D648
Glass Transition Temperature 154 °C DSC
Melting Temperature 303 °C DSC
CLTE - Flow (< 154°C) 7.7E-5 cm/cm/°C ASTM D696
Thermal Conductivity 0.25 W/m/K ASTM C177
Electrical Nominal Value Unit Test Method
Surface Resistivity 2.0E+16 ohms ASTM D257
Volume Resistivity 1.0E+16 ohms·cm ASTM D257
Dielectric Strength 75 kV/mm ASTM D149
Dielectric Constant (1 kHz) 2.10   ASTM D150
Dissipation Factor (1 kHz) 1.0E-3   ASTM D150
Flammability Nominal Value Unit Test Method
Flame Rating V-0   UL 94
Notes
2Stainless Steel
3Steel
4Galvanized Steel
5Aluminum
6Anodized Aluminum