AKROTEK® PAEK CF 30 black (5216)

2023-02-27

AKROTEK® PAEK CF 30 black (5216)
Polyetherketoneketone
30% Carbon Fiber
Product Description
AKROTEK® PAEK CF 30 black (5216) is a 30% carbon fibre reinforced polyetherketoneketone with high flexural strength and good sliding properties
Applications are mainly elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength and high stiffness in a temperature environment above 150°C
General
Filler / Reinforcement	Carbon Fiber, 30% Filler by Weight

Features	High Stiffness	High Strength

Uses	Aerospace Applications	Industrial Applications

	Automotive Applications	Medical/Healthcare Applications

Appearance	Black

Resin ID (ISO 1043)	PEKK CF30

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.4	g/cm³	ISO 1183
Spiral Flow^2, 3	72	cm	Internal Method
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	25000	MPa	ISO 527-2/1
Tensile Stress (Break)	250	MPa	ISO 527-2/5
Tensile Strain (Break)	1.4	%	ISO 527-2/5
Flexural Modulus⁴	24000	MPa	ISO 178
Flexural Stress⁴	365	MPa	ISO 178
Flexural Strain at Break⁵	1.8	%	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	40	kJ/m²	ISO 179/1eU
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	> 280	°C	ISO 75-2/A
8.0 MPa, Unannealed	195	°C	ISO 75-2/C
Melting Temperature⁶	340	°C	DIN EN 11357-1
Notes
²Mold Temperature: 195°C, Melt Temperature: 385°C, Injection Pressure: 2.00E+3 bar
³cross section of flow spiral: 7 mm x 3.5 mm
⁴2.0 mm/min
⁵2 mm/min
⁶10 K/min, DSC