| GAPEKK™ 3200G | |||
| Polyetherketoneketone | |||
| Product Description | |||
| Product Details: Ultra high performance thermoplastic polymer, unfilled Polyether Ketone Ketone (PEKK), semicrystalline granules suitable for injection molding and stock shapes extrusion, standard flow, Brown in color. | |||
| Application Areas: Suitable for high temperature applications, with high compressive strength & abrasion resistance, high chemical resistance & oil resistance etc. | |||
| General | |||
| Features | Good Abrasion Resistance | Good Flow | Oil Resistant |
| Good Chemical Resistance | High Heat Resistance | Semi Crystalline | |
| Uses | High Temperature Applications | ||
| Appearance | Brown | ||
| Forms | Granules | ||
| Processing Method | Extrusion | Injection Molding | |
| Physical | Nominal Value | Unit | Test Method |
| Density | 1.30 | g/cm³ | |
| Molding Shrinkage 2 | |||
| Flow | 1.0 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
| Durometer Hardness (Shore D, 23°C) | 88 | ASTM D2240 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus (23°C) | 4000 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 to 15 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 180 | MPa | ASTM D790 |
| Compressive Modulus | 2100 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 132 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 189 | °C | ASTM D648 |
| Continuous Use Temperature | 300 | °C | UL 746B |
| Glass Transition Temperature | 176 | °C | ASTM D3418 |
| Melting Temperature | 396 | °C | ASTM D3418 |
| Thermal Stability - Haake 3 | 20 | min | |
| Flammability | Nominal Value | Test Method | |
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Injection | Nominal Value | Unit | |
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 420 | °C | |
| Processing (Melt) Temp | 390 to 420 | °C | |
| Mold Temperature | 200 to 220 | °C | |
| Notes | |||
| 2420°C nozzle, 220°C Mold | |||
| 3GSRF 05/420°C, 60 rpm |