Halar@1400LC

Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Physical Properties Metric Comments Density  1.68 g/cc ASTM D792 Water Absorption at Saturation  <= 0.100 % ASTM D570 Linear Mold Shrinkage, Flow  0.0250 cm/cm ASTM D255 Melt Flow  450 - 600 g/10 min ASTM D1238 @Load 2.16 kg, Temperature 275 °C Mechanical Properties Metric Comments Hardness, Rockwell R  73 ASTM D785 Hardness, Shore D  69 ASTM D2240 Tensile Strength at Break  19.0 - 29.0 MPa 50 mm/min; ASTM D638 @Temperature 23.0 °C Tensile Strength, Yield  30.0 MPa 50 mm/min; ASTM D638 @Temperature 23.0 °C Elongation at Break  1.00 - 10.0 % 50 mm/min; ASTM D638 @Temperature 23.0 °C Elongation at Yield  1.00 - 10.0 % 50 mm/min; ASTM D638 @Temperature 23.0 °C Tensile Modulus  1.78 GPa 50 mm/min; ASTM D638 @Temperature 23.0 °C Flexural Strength  45.0 - 47.0 MPa 2.5 mm/min; ASTM D790 @Temperature 23.0 °C Flexural Modulus  1.69 GPa 2.5 mm/min; ASTM D790 @Temperature 23.0 °C Izod Impact, Notched   0.190 J/cm ASTM D256 @Thickness 3.20 mm, Temperature -40.0 °C 0.250 J/cm ASTM D256 @Thickness 3.20 mm, Temperature 23.0 °C Coefficient of Friction, Dynamic  0.2 vs. Itself; ASTM D1894 Coefficient of Friction, Static  0.2 vs. Itself; ASTM D1894 Taber Abrasion, mg/1000 Cycles  5 CS-17 Wheel, 500 g; ASTM D1044 Electrical Properties Metric Comments Volume Resistivity  5.50e+16 ohm-cm ASTM D257 Dielectric Constant  2.57 ASTM D150 @Frequency 1.00e+6 Hz Dielectric Strength  14.0 kV/mm ASTM D149 @Thickness 3.20 mm, Temperature 23.0 °C Thermal Properties Metric Comments CTE, linear, Parallel to Flow  100 µm/m-°C ASTM D696 Specific Heat Capacity  0.962 J/g-°C ASTM C351 @Temperature 23.0 °C Thermal Conductivity  0.150 W/m-K ASTM C177 Melting Point  234 °C Crystallization Temperature  222 °C Peak; ASTM D3418 Deflection Temperature at 0.46 MPa (66 psi)  109 °C Unannealed; ASTM D648 Deflection Temperature at 1.8 MPa (264 psi)  68.0 °C Unannealed; ASTM D648 Brittleness Temperature  20.0 °C Procedure A; ASTM D746 Glass Transition Temp, Tg  85.0 °C ASTM E1356 Flammability, UL94  V-0 UL 94 Oxygen Index  52.00% ASTM D2863 Descriptive Properties Availability (as of March 2019) Africa & Middle East; Asia Pacific; Europe; Latin America; North America Forms Pellets Processing Extrusion