3M™ Dyneon™ TFM™ Modified PTFE TFR 1502 A

3M™ Dyneon™ TFM™ Modified PTFE TFR 1502 A

2018-09-08 18:03:10

  

3M™ Dyneon™ TFM™ Modified PTFE TFR 1502 A  
Polytetrafluoroethylene    
Product Description:    
Modified PTFE for ram extrusion    
     
Features    
     
Tailor made for ram extrusion    
     
Excellent free-flowing characteristics with easy feeding  
     
Reduced deformation under load (cold flow)  
     
Good mouldability    
     
Low porosity and reduced permeability    
     
Excellent product smoothness    
     
Improved weldability    
     
     
Typical Applications    
     
Ram extrusion of rods and profiles with wall thickness preferably greater than 12mm
     
Ram extrusion of tubes with wall thickness preferably greater than 4 mm
     
Semi-finished articles    
     

General 　
Features  Good Flow Good Moldability Weldable
Uses  Profiles Rods Tubing
Processing Method  Ram Extrusion
Physical Nominal Value Unit Test Method
Density 2.16 g/cm³ ISO 12086
Apparent Density 0.8 g/cm³ ISO 60
Molding Shrinkage 2 (23.0 mm) 11 % Internal Method
Average Particle Size 800 µm ISO 13320
Hardness Nominal Value Unit Test Method
Shore Hardness (Shore D) 53 　 ISO 868
Mechanical Nominal Value Unit Test Method
Deformation Under Load 　 　 ASTM D621
23°C, 15 MPa 3 6 % 　
23°C, 15 MPa 4 14 % 　
Films Nominal Value Unit Test Method
Tensile Strength (500 µm) 35 MPa ISO 527-3
Tensile Elongation (Break, 500 µm) 500 % ISO 527-3
Thermal Nominal Value Unit Test Method
Thermal Conductivity 0.22 W/m/K DIN 52612
Electrical Nominal Value Unit Test Method
Surface Resistivity 1.00E+17 ohms IEC 60093
Volume Resistivity 1.00E+18 ohms·cm IEC 60093