| 3M™ Dyneon™ PTFE TF 2071Z | |||
| Polytetrafluoroethylene | |||
| Product Description: | |||
| PTFE fine powder for tubing, wire and cable applications | |||
| Features | |||
| Meets ASTM D 4895-04 Type I, Grade 1, Class C classification. | |||
| 3M™ Dyneon™ PTFE Paste TF 2071Z is the recommended grade for the manufacture of high quality tubing and wire and cable insulation up to RR of 1600:1 | |||
| High molecular weight PTFE powder, produced by the emulsion polymerization | |||
| Product grade with higher extrusion pressure and green strength value than 3M™ Dyneon™ PTFE Paste TF 2072Z | |||
| Wide processing range because of high RR | |||
| General | |||
| Features | High Molecular Weight | ||
| Uses | Insulation | Tubing | Wire & Cable Applications |
| Forms | Paste | Powder | |
| Processing Method | Ram Extrusion | Sintering | |
| Physical | Nominal Value | Unit | Test Method |
| Density 2 | 2.16 | g/cm³ | ISO 12086 |
| Apparent Density | 0.49 | g/cm³ | ISO 60 |
| Average Particle Size | 400 | µm | ISO 13320 |
| Films | Nominal Value | Unit | Test Method |
| Tensile Strength | 34.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break) | 410 | % | ISO 527-3 |
| Additional Information | Nominal Value | Unit | Test Method |
| Extrusion Pressure - reduction ratio 1600 | 50.0 | MPa | ASTM D4895 |
| Reduction Ratio | 20-1600:1 | Internal Method |