| LNP™ THERMOCOMP™ 2FL24 compound | |||
| Ethylene Tetrafluoroethylene Copolymer | |||
| 20% Glass Fiber | |||
| Product Description | |||
| LNP THERMOCOMP 2FL24 is a compound based on ETFE resin containing 20% Glass Fiber, 10% PTFE. Added feature of this grade is Wear Resistant. | |||
| Also known as: LNP* THERMOCOMP* Compound FP-EFL-4024 | |||
| Product reorder name: 2FL24 | |||
| General | |||
| Filler / Reinforcement | Glass Fiber, 20% Filler by Weight | ||
| Additive | PTFE Lubricant (10%) | ||
| Features | Good Wear Resistance | Lubricated | |
| Processing Method | Injection Molding | ||
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 7.0E-3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | |||
| -- 2 | 6450 | MPa | ASTM D638 |
| -- | 5010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 3 | 69 | MPa | ASTM D638 |
| Break | 67 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 6.5 | % | ASTM D638 |
| Break | 6.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4760 | MPa | ASTM D790 |
| -- 5 | 4990 | MPa | ISO 178 |
| Flexural Stress | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D256 |
| 23°C 6 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 6 | 92 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 20.0 | J | ASTM D3763 |
| -- | 8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 251 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 239 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 198 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 160 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.40E-05 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.40E-05 | cm/cm/°C | |
| Injection | Nominal Value | Unit | |
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Notes | |||
| 25.0 mm/min | |||
| 3Type I, 5.0 mm/min | |||
| 41.3 mm/min | |||
| 52.0 mm/min | |||
| 680*10*4 | |||
| 780*10*4 mm |