| Quadrant EPP Fluorosint® HPV | |||
| Polytetrafluoroethylene | |||
| Product Description | |||
| Mica-filled PTFE provides a unique blend of strength and dimensional stability along with an excellent wear enhancing additive technology. This product provides excellent wear and stability in addition to FDA compliance. | |||
| General | |||
| Filler / Reinforcement | Mica | ||
| Additive | Lubricant | ||
| Features | Good Dimensional Stability | Good Strength | |
| Good Stability | Good Wear Resistance | ||
| Agency Ratings | FDA Unspecified Rating | ||
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 2.05 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Saturation | 0.43 | % | |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness (R-Scale) | 52 | ASTM D785 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 1240 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 8.96 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 17.2 | MPa | ASTM D790 |
| Compressive Modulus | 503 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 27.6 | MPa | ASTM D695 |
| Shear Strength | 17.2 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.15 | Internal Method | |
| Wear Factor | 44 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact | 96 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 260 | °C | |
| Peak Crystallization Temperature (DSC) | 327 | °C | ASTM D3418 |
| CLTE - Flow 2 (-40 to 149°C) | 9.7E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 | |
| Additional Information | Nominal Value | Unit | Test Method |
| Limiting Pressure Velocity 4 | 0.657 | MPa·m/s | Internal Method |
| Notes | |||
| 1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier. | |||
| 268°F | |||
| 3EOS/ESD S11.11 | |||
| 44:1 safety factor |