OXPEKK® Bioflex™

2023-02-27

OXPEKK® Bioflex™      
Polyetherketoneketone      
Carbon Fiber      
Product Description
OXPEKK ® BioFlex™ smart materials are composed of multiple layers of continuous carbon fibers and thermoplastic OXPEKK® resin. The fibers are orientated within the part, so that sitffness is defined by firber direction. The isotropic nature of metallic and conventional polymeric materials are overcome, thus opening a new era of dynamic stabilization and motion preservation.
 
To date orthopedic implant design engineers have relied upon complex mechanical assemblies and articulting surfaces in order to preserve motion. OXPEKK® Bioflex™ introduces a new and dynamic tool for the orthopedic OEM's via the combination of smart materials and established design techniques.
 
OXPEKK® Bioflex™ can be supplied in oriented laminated plates of thickness 1 - 10mm up to 60cm square, semi-finished thermoformed 3D parts waterjet cut and hot-formed from oriented plates and solid unidirectional rods. Common orientations include Cross-Ply (0/90), Unidirectional, Quasi-Isotropic (-45/0/45/90), Torsional-Ply (-45/45). Parts can be readily machined on conventional equipment such as is used for other carbon fiber composites.
 
OXPEKK® Bioflex™ is available for long-term implants with an executed supply agreement.
General  
Uses  Body Implants Laminates Medical/Healthcare Applications
Forms  Fiber

Mechanical Nominal Value Unit Test Method
Tensile Modulus     ASTM D638
-- 2 10700 MPa  
-- 3 146000 MPa  
Tensile Strength     ASTM D638
-- 4 398 MPa  
-- 2 57.0 MPa  
-- 3 2510 MPa  
Compressive Modulus     ASTM D695
-- 5 10700 MPa  
-- 6 123000 MPa  
Compressive Strength     ASTM D695
-- 4 335 MPa  
-- 5 238 MPa  
-- 6 1620 MPa  
Notes      
290° Tensile      
30° Tensile      
4Open Hole      
590° Compressive      
60° Compressive      