| Ajedium™ Films -- Radel® R-5100 NT15 | |||
| 聚苯砜 | |||
| 产品说明 | |||
| Radel® polyphenylsulfone is an amorphous thermoplastic material that offers exceptional hydrolytic stability, and toughness superior to other commercially available, high-temperature flims. | |||
| PPSU films have high deflection temperatures and outstanding resistance to environmental stress cracking. The polymer is inherently flame retardant. The excellent thermal stability makes films suitable for applications where very low shrink at high temperatures are needed. PPSU films also have good electrical properties. | |||
| Radel® film is white in color. | |||
| 总体 | |||
| 特性 | 高 ESCR（抗应力开裂） | 热稳定性，良好 | 水解稳定 |
| 良好的电气性能 | 韧性良好 | 阻燃性 | |
| 用途 | 电池 | 航空航天应用 | 医疗/护理用品 |
| 电气/电子应用领域 | 汽车领域的应用 | ||
| 飞机应用 | 食品服务领域 | ||
| RoHS 合规性 | RoHS 合规 | ||
| 外观 | 不透明 | ||
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 比重 | 1.3 | g/cm³ | ASTM D792 |
| 吸水率 (24 hr) | 0.37 | % | ASTM D570 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
| 薄膜厚度 - 经测试 | 25 | µm | |
| 割线模量 | ASTM D882 | ||
| MD | 1590 | MPa | |
| TD | 1980 | MPa | |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服 | 68 | MPa | |
| TD : 屈服 | 59 | MPa | |
| MD : 断裂 | 92 | MPa | |
| TD : 断裂 | 70 | MPa | |
| 伸长率 | ASTM D882 | ||
| MD : 屈服 | 9.2 | % | |
| TD : 屈服 | 6.8 | % | |
| MD : 断裂 | 140 | % | |
| TD : 断裂 | 100 | % | |
| 落锤冲击 | 540 | g | ASTM D1709 |
| 面积系数 | 149 | ft²/lb/mil | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 (1.8 MPa, 未退火, 3.18 mm) | 207 | °C | ASTM D648 |
| 玻璃转化温度 | 220 | °C | ASTM E1356 |
| 线形热膨胀系数 - 流动 (3.18 mm) | 5.60E-05 | cm/cm/°C | ASTM D696 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 体积电阻率 | 9.00E+15 | ohms·cm | ASTM D257 |
| 介电强度 (0.0250 mm) | 190 | kV/mm | ASTM D149 |
| 介电常数 | 1.38 | ASTM D150 | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| 极限氧指数 | 38 | % | ASTM D2863 |
| 补充信息 | |||
| Standard Thicknesses and Widths | |||
| Widths are available from 22" (559 mm) to 56" (1422 mm). | |||
| Products with widths <22 inches or >56 inches are available upon request. | |||
| Tolerances for widths are +/- 4mm. | |||
| For PPSU film, the standard thicknesses are 25 microns (1 mil) to 1016 microns (40 mil). | |||
| Surface Finishes | |||
| Standard surface finish is P/M (polished / matte). | |||
| Custom finishes of P/P (polished / polished) and M/M (matte / matte) are available. | |||
| Packaging | |||
| Film is supplied in a roll form of high quality, cardboard core of 3" (76mm) or 6" (152mm). | |||
| PVC cores are available upon request in 3" and 6" sizes. | |||
| Labeling | |||
| Products are labeled to comply with national and international standards. | |||
| Labels include product grade, unique batch number, roll length, roll width, product thickness, and net weight. | |||